Stainless Steel 304 / 304L Patta & Patti, SS 304 / 304L Patta, Steel Patti, SS 304 / 304L Patta & Patti, ASTM A240 304 / 304L Stainless Steel Patta, Stainless Steel 304 / 304L Patti, SS UNS S30400 / S30403 Patta, SS DIN 1.4301 / 1.4307 Patti Suppliers In India.
National India. Co (India) is a known distributor of SS 304 / 304L Patta Patti, which is the most widely utilized grade and known as the classic 18/8 (18% chromium, 8% nickel) stainless steel. Purchase Stainless Steel 304 / 304L Patta Patti at very competitive price from us. ASTM A240 Type 304 / 304L Patta Patti was initially called 18-8 which represented its chromium and nickel content. ASTM A240 Stainless Steel 304 / 304L Patti is utilized in kitchen benches, sinks, troughs, equipment, and appliances. ASME SA 240 Type 304 / 304l Patta has great mechanical properties and corrosion resistance. The deliberately controlled chemical composition of ASME SA 240 SS 304 / 304L Patti enables them to be deep drawn more seriously than AISI types 301, without intermediate annealing. In the annealed condition, ASME SA 240 Stainless Steel 304 / 304L Patta Patti is basically non-magnetic and becomes slightly magnetic with the application of cold work. SS 304 / 304L Patta has great low-temperature properties and reacts well to hardening by cold working. Stainless Steel UNS S30400 / S30403 Patta Patti is an austenitic alloy, which implies that a non-magnetic solid solution of ferric carbide or carbon in iron is utilized in giving this stainless steel its corrosion-resistant properties.
Stainless Steel DIN 1.4301 / 1.4307 Patta Patti displays great machinability and have phenomenal weld-ability characteristics with or without the addition of filler metals. SS DIN 1.4301 / 1.4307 Patta Patti is used in all industrial, commercial and domestic fields in view of its good corrosion and heat resisting properties. Therefore, SS 304 / 304L Patta Patti is frequently utilized for a variety of household and industrial applications, for example, screws, machinery parts, car headers, and food-handling equipment. Grade 304 / 304L Stainless Steel Patti is also utilized in the architectural field for exterior accents, for example, water and fire features. Grade SS 304 / 304L Patta Patti is as well utilized in moisture separator re-heaters, feed-water tubes, stator bars, heat exchangers, and many more. So, everything from stovetops to ball point pen barrels to flatware to fasteners has been fabricated from Type 304 / 304L Stainless Steel Patta minimum carbon in Type 304 / 304L SS Patta Patti limits chromium carbide precipitation due to welding and its susceptibility to inter-granular corrosion.
AISI Type 304 / 304L Stainless Steel Patta Patti has magnificent toughness, even down to cryonegic temperatures which are characterized as very low temperatures. The balanced austenitic structure of AISI 304 / 304L Stainless Steel grade empowers it to be severely deep drawn without intermediate annealing, which has made this grade dominant in the manufacture of drawn stainless parts, for example, sinks, hollow-ware and saucepans.
You can get the exact material according to your requirement at the least possible price. We also provide Reworks, FOB, CFR, CIF, and door to door delivery prices. The materials we offer are completely verifiable, right from raw material test certificate to the final dimensional statement. E-guarantee to give a response within 24hours working hours (usually in the same hour).You can also get stock alternatives, mill deliveries with minimizing manufacturing time. We are completely dedicated to our customers. If it will not possible to meet the customer requirements after examining all options, we will not mislead by making false promises which will create good customer relations.
|Standard||:||ASTM A 240, ASME SA 240|
|Thickness||:||1 MM To 100 MM|
|Hardness||:||HRB 62 to 180 – HV 140 to 1250|
|Tensile Strength||:||As required up to 1450MPA|
Chemical Composition of SS 304 / 304L Patta & Patti:
|SS 304||8-11||18-20||2 Max||8-11||0.045 Max||0.03 Max||1.0 Max|
|SS 304L||8-11||18-20||2 Max||8-12||0.045 Max||0.03 Max||1.0 Max|
Mechanical Properties of SS 304 / 304L Patta & Patti:
|Element||Tensile Strength||Yield Strength||Elongation||Density||Melting Point|
|304||Psi – 75000||Psi – 30000||35%||8.0 g/cm3||1400 °C (2550 °F)|
|304L||Psi – 75000||Psi – 30000||40%||8.0 g/cm3||1400 °C (2550 °F)|